| SL
5510 Resin |
|
| Typical Properties: Liquid Resin SL 5510 |
| Measurement |
Condition |
Value |
|
| Appearance |
|
Clear |
|
| Density |
@ 25°C (77°F) |
1.13 g/cc |
|
| Viscosity |
@ 30°C (86°F) |
180 cps |
|
| Penetration Depth (DP)* |
SLA350/3500
SLA 5000 |
4.1 mils
4.3 mils |
|
| Critical Exposure (Ec)* |
SLA350/3500
SLA 5000 |
11.4 mJ/cm2
11.2 mJ/cm2 |
|
| Part building layer thickness |
|
0.05 mm (0.002 in)*
0.10 mm (0.004 in)*
0.15 mm (0.006 in)* |
|
|
| Typical Properties: Post Cured Part |
| Measurement |
Method |
Value |
|
| Tensile strength |
ASTM D 638 |
77 Mpa (11,100 psi) |
|
| Tensile modulus |
ASTM D 638 |
3,296 Mpa (478,000 psi) |
|
| Elongation at break |
ASTM D 638 |
5.4% |
|
| Flexural strength |
ASTM D 790 |
99 Mpa (14,400 psi) |
|
| Flexural modulus |
ASTM D 790 |
3,054 Mpa (443,000 psi) |
|
| Impact strength, notched |
ASTM D 256 |
27 J/m (0.5 ft-lbs/in) |
|
| Hardness |
ASTM D 2240 |
86 Shore D |
|
| Glass deflection temp |
DMA, E" peak (UV postcure)
ASTM D 648 |
68°C (154°F) |
|
| Heat deflection temp |
ASTM D 648
@66 psi
@264 psi |
50°C (122°F)
43°C (109°F) |
|
|
@66 psi (UV postcure) |
62°C (144°F) |
|
|
@66 psi [UV+2 hrs @80°C (176°F)]** |
87°C (189°F) |
|
| Heat deflection temp |
@264 psi (UV postcure) |
53°C (127°F) |
|
|
@264 psi [UV+2 hrs @80°C (176°F)]** |
76°C (169°F) |
|
|
* Not applicable to all part geometries or build parameters
** 90 minute UV postcure+2hrs @ 80°C thermal postcure
Specifications are subject to change without notice.
|
 |
|