| Typical Properties: Liquid Resin SL 5520 |
| Measurement |
Condition |
Value |
|
| Appearance |
|
Clear |
|
| Density |
@ 25°C (77°F) |
1.15 g/cc |
|
| Viscosity |
@ 30°C (86°F) |
444 cps |
|
| Penetration Depth (DP)* |
SLA350/3500
SLA 5000 |
4.8 mils
4.4 mils |
|
| Critical Exposure (Ec)* |
SLA350/3500
SLA 5000 |
19.9 mJ/cm2
13.0 mJ/cm2 |
|
| Part building layer thickness |
|
0.10 mm (0.004 in)*
0.125 mm (0.005 in)* |
|
|
| Typical Properties: Post Cured Part** |
| Measurement |
Method |
Value |
|
| Tensile strength |
ASTM D 638 |
26-33 Mpa (3,800-4,800 psi) |
|
| Tensile modulus |
ASTM D 638 |
1,034-1,379 Mpa (150,000-200,000 psi) |
|
| Elongation at break |
ASTM D 638 |
23-43% |
|
| Flexural strength |
ASTM D 790 |
29-41 Mpa (4,200- 6,000 psi) |
|
| Flexural modulus |
ASTM D 790 |
689-896 Mpa (100,0000- 130,000 psi) |
|
| Impact strength, notched |
ASTM D 256 |
59 J/m (1.1 ft-lbs/in) |
|
| Hardness |
ASTM D 2240 |
80 Shore D |
|
| Glass deflection temp |
DMA, E" peak (UV postcure)
ASTM D 648 |
34°C (93°F) |
|
| Heat deflection temp |
@66 psi (UV postcure) |
44°C (111°F) |
|
|
* Not applicable to all part geometries or build parameters
** 90 minute UV postcure+2hrs @ 80°C thermal postcure
Specifications are subject to change without notice.
|
 |