| SL
5530HT Resin |
|
| Typical
Properties: Liquid Resin SL 5530HT
|
| Measurement |
Condition |
Value |
| Appearance |
|
Clear |
| Density |
@
25° C (77° F) |
1.19
g/cc |
| Viscosity |
@
25° C (77° F) |
310
cps |
| Penetration
depth (Dp) |
|
5.4
mils (5.6 mils SLA 350/3500) |
| Critical
exposure (Ec) |
|
8.9
mJ/cm² (9.4 mJ/cm² SLA 350/3500) |
| Part
building layer thickness* |
|
0.05
mm (0.002 in)*
0.10 mm (0.004 in)*
0.15 mm (0.006 in)* |
|
|
| Typical
Properties: Post-Cured Part** |
| Measurement |
Condition |
Value
90 minute UV postcure |
Value
90 minute UV postcure plus 160° C (320° F) thermal postcure for 2
hours |
| Tensile
strength |
ASTM
D 638 |
56-61
MPa (8,300-8,900 psi) |
47-61
MPa (6,800-8,900 psi) |
| Tensile
modulus |
ASTM
D 638 |
2,889-3,144
MPa (419,000-456,000 psi) |
3,585-3,758
MPa (520,000-545,000 psi) |
| Elongation
at break |
ASTM
D 638 |
3.8-4.4% |
1.3-2.9% |
| Flexural
strength |
ASTM
D 790 |
63-87
MPa (9,100-12,600 psi) |
96-108
MPa (13,900-15,700 psi) |
| Flexural
modulus |
ASTM
D 790 |
2,620-3,240
MPpa (380,000-470,000 psi) |
3,496-3,634
MPa (507,000-527,000 psi) |
| Impact
strength, notched |
ASTM
D 256 |
21
J/m (0.4 ft-lbs/in) |
21
J/m (0.4 ft-lbs/in) |
| Hardness,
Shore D |
DIN
53505 |
88 |
90 |
| Glass
transition temp, Tg |
DMA,
E" peak (UV postcure) |
79°
C (174° F) |
122°
C (252° F) |
| Heat
deflection temp |
ASTM
D 648
@66 psi |
>
80° C (176° F) |
>
200° C (392° F) + |
|
|
*
Not applicable to all part geometries or build parameters.
Specifications
are subject to change without notice.
|
|